Water - Based Coating Low Gloss Water Epoxy Paint For Automatic Line Spraying

Ask Latest Price
Video Channel
Brand Name :KINTE
Model Number :AE-7223
Certification :ROHS, ISO90001, ISO14000, Reach
Place of Origin :China
MOQ :1000kg
Price :Negotiable
Payment Terms :L/C, T/T, D/P
Supply Ability :10,000 tons per year
Delivery Time :10 working days
Packaging Details :Component A: 18kg/barrel, Component B: 1.5kg/barrel or 2.0kg/barrel
Resin Type :Waterborne modified epoxy resin
Curing Agent Type :Modified polyamine curing agent
Mixing proportion (Weight) :Main agent: curing agent = 11:1
Mixing proportion (Volume) :Main agent: curing agent = 8.2:1
Gloss :Semi gloss (25 ~ 35%)
Recommended Dry Film Thickness :90-120µm
Applicable Substrate :Cast iron, galvanized sheet, etc.
Application :Elector-mechanical equipment, special vehicles, etc.
more
Contact Now

Add to Cart

Find Similar Videos
View Product Description

Semi Gloss Epoxy Water Paints Liquid Coating for Decoration and Anti-corrosion Protection

Introduction

Water-based paint is a paint that uses water as a diluent and does not contain organic solvents. It is non-toxic, non-irritating, harmless to the human body, and does not pollute the environment. The paint film is plump, crystal clear, flexible, and resistant to water, abrasion, and aging , anti-yellowing, fast drying, easy to use and so on.

AE-7223 is widely used in the surface coating of metal substrates of elector-mechanical equipment (Like: Air conditioning refrigeration unit), special vehicles, engineering machinery and other products, plays a good role in decoration and anti-corrosion protection, and is suitable for high-pressure airless / mixed gas spraying and automatic line spraying.

Advantages

1. Using water as a solvent saves a lot of resources; eliminates the risk of fire during construction; reduces air pollution; only uses a small amount of low-toxic alcohol ether organic solvents to improve the working environment. The organic solvent (accounting for paint) of general water-based paint is between 5% and 15%, while the cathodic electrophoretic paint has been reduced to less than 1.2%, which has a significant effect on reducing pollution and saving resources.

2. Water-based coatings can be directly coated on wet surfaces and in humid environments; they have good adaptability to material surfaces and strong coating adhesion.

3. The coating tools can be cleaned with water, which greatly reduces the consumption of cleaning solvents and effectively reduces the damage to construction personnel.

4. The electrophoretic coating film is uniform and smooth. Good flatness; inner cavity, welds, corners, and edges can be coated with a certain thickness of coating film, which has good protection; electrophoretic coating has the best corrosion resistance, thick film cathodic electrophoretic coating The salt spray resistance can reach up to 1200h.

Specifications:

Resin Type

Waterborne modified epoxy resin

Modified polyamine curing agent

Gloss Semi gloss (25 ~ 35%)
Viscosity of original paint (rotary viscometer, 64# rotor, 60rpm, 25℃)

Component A: 2000-2500mps;

Component B: 500-1000mps

Proportion (g/ml)

Component A: 1.41±0.05;

Component B: 1.05±0.03

Mass solid content (105℃×3h) 60±2%
Volumetric solid content 41±3%
Recommended dry film thickness 90-120µm
VOC ≤80g/L
Mixing proportion (weight) Main agent: curing agent = 11:1
Mixing proportion (Volume) Main agent: curing agent = 8.2:1
Storage life 6 months

◎Film Properties:

Test Item Result

Drying time

(temperature: 25℃, humidity: 80% RH)

Surface dry time: 1h;

Ultimate dry time: 24h

Fully cured in 7 days
Using drier: 40-80℃×20min~40min
Adhesive(1mm,grade) 1
Pencil hardness HB
Impact (50cm) Pass
Flexibility 2mm
Neutral salt spray resistance 360-600h
Water resistance (normal temperature deionized water) 1000h

Instructions

Composition Component A & B
Mix proportion 11:1 (Weight ratio)
Mix method After mixing component A, add component B and fully mix evenly
Diluent Deionized water
Curing period(25℃) 15-20min
Pot-life(25℃) 2h
Pretreatment of substrate The substrate shall be polished and make sure to be clean, dry, rust-free, oil-free, etc.
Construction viscosity 7500-8800mPa﹒s(25℃)
Applicable substrate Cast iron, galvanized sheet, carbon steel, cast aluminum and other metal substrates
Storage life

6 months.

Use it within the storage period to avoid affecting the quality;

The coating (including curing agent and diluent) shall be sealed and stored in a cool place.

Keep away from water, leakage potential, sunscreen, high temperature and fire source.

Package

Component A: 18kg/barrel

Component B: 1.5kg/barrel or 2.0kg/barrel

Attention:

  • The surface of the substrate must be clean and dry, and meet the requirements.
  • Component A & B should be mix according to the weight ratio of 12:1. Dilute with 0-3% deionized water, use it after curing for 15min, and use it up within the pot-life which is 2h under 25℃. The higher the temperature, the shorter the pot-life.
  • The tools used during construction must be dry and clean.
  • Clean tools and equipment with water immediately after construction.
  • It is strictly prohibited to contact with acid, alkali, oily paint and organic solvent during paint preparation and coating.
  • No more than 400μm films can be formed at one time, otherwise sagging will occur.
  • During construction, drying or curing, the relative humidity should be lower than 80% and the temperature higher than 5 ℃, otherwise the paint film cannot be completely cured.
  • Do not press or rub heavily to avoid damage to the paint film or contact with organic solvents and water before the paint film is completely dried.
  • Keep the construction site well ventilated and wear necessary protective equipment.

Water - Based Coating Low Gloss Water Epoxy Paint For Automatic Line SprayingWater - Based Coating Low Gloss Water Epoxy Paint For Automatic Line Spraying

Water - Based Coating Low Gloss Water Epoxy Paint For Automatic Line Spraying

Water - Based Coating Low Gloss Water Epoxy Paint For Automatic Line SprayingWater - Based Coating Low Gloss Water Epoxy Paint For Automatic Line SprayingWater - Based Coating Low Gloss Water Epoxy Paint For Automatic Line Spraying

Company Profile:

Kinte Materials Science and Technology Co., Ltd. is subordinate to China Machinery Industry Corporation (a key state-owned enterprise directly managed by SASAC, ranking 284 among the world's top 500 in 2021). It is a national high-tech enterprise under China National Electric Apparatus Research Institute Co., Ltd. (Stock Code: 688128), a listed enterprise on the SSE STAR MARKET. Focusing on the R & D, production, and sales of environmentally friendly coatings (powder coatings, waterborne industrial coatings) and powder coating resins, the company is committed to improving the global market competitiveness of China's environmentally friendly coating industry. Now it has become the leader and promoter in China’s technological development of environmentally friendly coatings as well as polyester resins for powder coatings!

We have gained ISO9001 and ISO14000, ISO18001, RoHS, UL certification and QUALICOAT Certificate. Due to the excellent and stable quality, our products always enjoy high reputation at home and oversea, and were sold to more than 30 countries. Our clients include many top air conditioning manufacturers in the world such as GREE, Midea, TICA, TRANE, etc.

We unremittingly stick at the business principle of “Quality is the life, adhere to first-class technology, first-class quality, first-class cost and first-class brand”. We would like to provide a complete set of services and solutions for both domestic and abroad customers and would like to go forward to brilliant future with you together.

Inquiry Cart 0